Alloy (V) DCCLIV Pre picta Aluminium Coil

Alloy (V) DCCLIV Pre pingitur Aluminium Coil Usus est Aluminium Alloy Aa5754 ut basi materia. Est enim non-calor-treatable membrum de 5xxx series, propria per altum magnesium content (2.6-3.6%), quod praebet optimum corrosio resistentia, formability et weldility. Developed pro Applications requiring a statera roboris et ductility, id est late in marine environments, automotive structurae, pressura vasa et cryogenic systems.

Request a Quick Quote

Chemical compositionem

Elementum	Content (%)
Aluminium (al)	Statera
Magnesium (mg)	4.0.-4.9
Manganese (mn)	0.40-1.0
Silicon (Si)	≤0.40
Ferrum (fe)	≤0.40
Zinc (ZN)	≤0.25
Aeris (cu)	≤0.10
Chromium (CR)	0.05-0.25
Titanium (TI)	≤0.20
Alia (se)	≤0.05
Totalis impudicitities	≤0.15

Note: Paulo altius Aluminium Puritas (vs. ML) reduces immunditia campester, porro enancing corrosio resistentia et electrica conductivity.

Clavem proprietatibus

Mechanica proprietatibus

Res	Temper: O	Temper: H12 / H32	Temper: H14 / H34	Temper: H16 / H36	Temper: H18 / H38
Tensile viribus	195-240MPA	220-260 MPA	245-285 MPA	270-30 MPA	CCXCV -335 MPA
Release fortitudinem (0.2% Offset)	80-120 MPA	165-200 MPA	205-240 MPA	230-270MPA	260-300 MPA
Elongatio ad confractus	22-28%	16-20%	12-16%	8-12%	6-10%
Durness (B) Rockwell	Non opus indurare	Humilis	Medium	Altum	PERPREPIDUS

Physica proprietatibus

Res	Valor
Densitas	2.48 G / CM³
Point liquescens	527-621 ° C
Scelerisque conductivity	190-225 W / M K
Electrical Conductivity	30-40% iacs
Thermal expansion coefficient	13.1-13.3 × 10⁻⁶ / C (20-100 ° C)
Modulum elasticitatis	69gpa
Poisson scriptor rate	0.33
Imprimis calor capacitatem	0.22 BTU / (LB ° F) (CMXX J / (KG ° F)):
Tondendas modulum	XXVI GPA
Mole modulus	LXIX GPA